Pet Titanium White Mother Granules (Injection Molding) (PET0TD60-1)
Product Manual
Product Description:
This product is a titanium -WHITE MOTHER -in -CHIP With Pet Res ReSin as a Carrier. It is Mainly used for injection molding and extruded propucts of pet resin and pet. Composition Materials. The Product has low viscil, Good Decentralization, Strong Coloring Ability, and good processing performance.
Product Advantages:
★ This Product, COLORORING PROPERTIES, and the Mechanical Properties of the Color Materials Are Small, and It Dors Not Affect the Procase PROCESS of The product;
★ This product can be mixed directly with the mailial account to the problem, and can be dried with the material and processed directly;
★ Meet the requirements of dust -Free, easy to transport and mix;
Technical Parameter:
|
project |
Unit |
standard |
|
Exterior |
|
Titanium granules |
|
Volatility (105 ° C/2HR) |
% |
≤ & nbsp; 0.5 |
|
Effective content |
% |
60 |
|
Substrate |
|
PET |
Instructions:
Reference dosage: 1-3%.
Product storage
Use aluminum foil bag bag vacuum packaging, net weight 5kg (can be according to customer requirements).
Application examples
▲ 2KGPET resin+0.04kgpet0td60-1 mother granules mixed injection molding sample test
|
Test items |
Test method |
Unit |
Test data |
|
stretch strength tensile Stringth |
gb/t & nbsp; 1040-2018 |
MPA |
64.6 |
|
Fracture and elongation Elongation at break |
% |
36.4 |
|
|
Bending strength Flexural Streangth |
gb/t & nbsp; 9341-2008 |
MPA |
80.0 |
|
Bending modulus Flexural Modulus |
MPA |
1884 |
|
|
Strong impact of the cantilever gap Izod Impact Streangt & Nbsp; (V-NOTCHED) |
GB/T 1843-2008 |
kj/m2 |
5.1 |
|
Thermal deformation temperature (TFF1.8) Heat Deflection Temp (TFF1.8) |
GB/T 1634.2-2019 |
℃ |
70.9 |
|
density Density |
GB/T 1033-2008 |
g/cm3 |
1.36 |
|
Melofing quality flow rate (270 ° C, 2.16kg) Melt Mass Flow Rate |
GB/T 3682-2018 |
g/10min |
140 |
|
gray score ASH Content |
gb/t & nbsp; & nbsp; 9345-2008 |
% |
1.17 |